1.1121對應牌號

時間：2022/3/7閱讀：910
分享：
Chemical composition % of steel C10E (1.1121): EN 10084-2008
Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for thepurpose of finishing the heat.
Steels with improved machinability as a result of the addition of lead or higher sulfur contents, depending on the manufacturing process up to around 0.1 % S, may be supplied on request. In this case, the upper limit of the manganese content may be increased by 0.15 %
CSiMnPS
0.07 - 0.13max 0.40.3 - 0.6max 0.035max 0.035

Mechanical properties of steel C10E (1.1121)



Rm - Tensile strength (MPa) (+A)430


Rm - Tensile strength (MPa) (+CR)830


Rp0.2 0.2% proof strength (MPa) (+A)345


A - Min. elongation Lo = 80 mm (%) (+A)26
Brinell hardness (HBW): (+A)131
Brinell hardness (HBW): (+N)85 - 140
Rockwell B hardness ( HRB or RB): (+A)73
Vickers hardness ( HV): (+)135
Vickers hardness ( HV): (+CR)250
Properties of steel C10E (1.1121)
Weldability: It is a soft carbon-steel, easily cold machinable and weldable without any particular precautions.
Equivalent grades of steel C10E (1.1121)
Warning! Only for reference
EU
EN		Germany
DIN,WNr		France
AFNOR		England
BS		Italy
UNI		Spain
UNE		Russia
GOST		Inter
ISO
C10E
Ck10
Ck15
XC10
XC12
045M10
CS12
C10
C15
C10k
08
10
C10
C15M2